Name: China Customized Cast Basalt Lined Elbow Manufacturers Suppliers Factory - Good Price - Zibo Chenyi
Brand: Chenyi
SKU: 246246435

Description

Technical Parameters

Zibo Chenyi Advanced Materials Co., Ltd. is one of the leading manufacturers and suppliers of cast basalt lined elbow in China, also supports customized service. If you're going to buy CE approved cast basalt lined elbow made in China, welcome to get quotation from our factory. Quality products and low price are available.

Factory Directly Sale Cast Basalt Lined Pipes /Cast Basalt Lined Elbow

Cast Basalt is a high-performance industrial material made from natural basalt as the main raw material, which is formed by melting at high temperature and then cast. Its Mohs hardness can reach 8, which is several dozen times that of ordinary steel. It possesses excellent wear resistance, corrosion resistance and compressive strength (compressive strength can reach 800 MPa).

The Cast Basalt Lined Elbow is a pipe fitting made of basalt cast stone composite material. It has high wear resistance, corrosion resistance and high temperature resistance, and is widely used in industrial fields such as metallurgy, power and mining.

Rugular Size Of Cast Basalt Lined Elbow

Normal Diameter	DN80~600	The detailed specifications are based on factual conditions
Thickness of Wear-resistant Liner(mm)	20~50mm
Thickness of Steel	4~8mm

Remarks: Other sizes are available upon your requests

Cast Basalt Technical Data Sheet

The Technical Parameter for Cast Basalt
S/N	Item	Performance Index
1	Chemical Composition	Cast Basalt (FeO+SiO2)
2	Mohs Hardness	SRPS EN 101 min 8˚
3	Specific Density	SRPSEN993-1 2900-3000g/m3
4	Water Absorption	SRPS EN ISO 10545-3 0%
5	Compressive Strength(25)	SRPS EN 993-5 300-450 Mpa
6	Bending Strength	SRPS EN 993-6 min 45 Mpa
7	Resistance to abrasion depth of max	Loss 110 mm3
8	Heat resistance	min 300℃
9	Resistance to temperature shock	min.temp. difference 150℃
10	Hardness	≥720kg/mm
11	Flexural Strength(25)	≥60MPa
12	Elasticity Modulus	1.67×10
13	Using Temperature	800-900℃

Production Process

1. Centrifugal casting process‌: Through high-temperature centrifugal technology, a dense ceramic layer is formed, ensuring material uniformity and reducing the weight by 50% compared to ordinary cast stone pipes.

2. Spot welding assembly process: Use high-temperature resistant adhesive to fix the aluminum oxide ceramic sheet, and combine with spot welding technology to enhance the stability.

Material Characteristics and Product Advantages

Using cast basalt stone composite material, with a 10mm thick wear-resistant ceramic layer (with Mohs hardness above 9) on the inner wall, it is suitable for scenarios involving the transportation of granular materials and corrosive media.
‌Design features: Both ends are equipped with live flange connections, facilitating installation and commissioning; the inner wall is smooth (with a clear resistance coefficient of 0.0193), resulting in low operating resistance.

Working temperature: Can operate stably for a long time within the range of -50℃ to 700℃, with outstanding high-temperature resistance performance.

Performance advantages:
Malleability: Suitable for inner linings of desulfurization slurry pipes in power plants and inclined troughs in mines, etc., which are prone to wear.
Corrosion resistance: Ideal material for chemical transmission pipelines and liners of acid washing equipment.
High hardness: However, it has relatively high brittleness and should avoid bearing bending tensile stress.

Main Application Fields

The Cast Basalt Lined Elbow is mainly used in the coal transportation, pulverization and ash discharge systems of the metallurgical and power industries, as well as the material conveying pipelines in the mining and coal industries. It can extend the service life of equipment and reduce maintenance costs.